Pa66 Gf45
Pa Gf45

PA66 GF45 (A2011I) for Engineering Plastics

PA66 GF45 is a 45% glass fiber reinforced polyamide 6.6 with high stiffness and strength.

Typical Application of PA66 GF45 (A2011I)

PA66 45%GF HB grade is applied to the gear field, it requires high strength, high toughness and dynamic balance and applied to the field of sports equipment and electrical tools, it requires high toughness, low temperature resistance, and low cost. Commonly used as mechanical housing.

Processing Detail of PA66 GF45 (A2011I)

Processing Detail of PA66 GF45 (A2011I)

Other Details of PA66 GF45 (A2011I)

Physical Property

Ash(45.0% 1 ISO3451/1)
Conditioned600°C*2h
Density(1495Kg/m3 1 ISO1183)
Conditioned23°C
Shrinkage Parallel Flow(0.1-0.3% 1 ISO294-4)
Shrinkage Vertical Flow(0.4-0.6% I ISO294-4)

Mechanical Properties

Tensile strength (204.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.8% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (16.5 KJ/m2 IISO179)

Conditioned

1.0J

Flexural Strength (332MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (13547 MPa I ISO178)

Conditioned

2mm/min

Thermal Property

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(258*C I ISO75)

Conditioned

1.8MPa

Flammability Class

(HB 1UL94)

Conditioned

mm

Injection Molding Conditions

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

290-310°C

Nozzle Temperature

290-310*C

Tooling Temperature

80-100*C

* Molding conditions are just for reference, please make an adjustment based on the actual situation!