Pa6 6gf35
Pa 6.6 Gf35

PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics

PA66 is nylon 66, namely polyamide 66. GF is glass fiber. Generally expressed as PA66 GF35, that is, 35% glass fiber is added to nylon 66.

Typical Application of PA66 GF35 (A2000G)

It is applied to lamp holder cover and cooling fan, gears and various electronic connectors, wear-resistant parts of elevators, and internal and external structural parts around the engine such as cooling fan.

Processing Detail of PA66 GF35 (A2000G)

Processing Detail of PA66 GF35 (A2000G)

Other Details of PA66 GF35 (A2000G)

Physical Property

Ash

(35.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1407Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(0.2-0.4 % 1 ISO294-4)

Shrinkage Vertical Flow

(0.5-0.8% I ISO294-4)

Mechanical Properties

Tensile strength (193.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.6% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (15.0KJ/m2 IISO179)

Conditioned

1.0J

Flexural Strength (291MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (10069 MPa I ISO178)

Conditioned

2mm/ min

Thermal Property

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(255*C I ISO75)

Conditioned

1.8MPa

Flammability Class

(HB 1UL94)

Conditioned

mm

Injection Molding Conditions

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

280-300°C

Nozzle Temperature

280-300*C

Tooling Temperature

80-100*C

* Molding conditions are just for reference, please make an adjustment based on the actual situation!

Your satisfaction is important to us! Email us your questions about engineering plastic and masterbatch products and more.