Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding.
The material PA66 GF30 thermal stability typically works for automobile engines, motor accessories such as engine covers, cooling fans, coil frames,and plugs, sockets and spools in electrical and electronic fields.
Physical Property
Ash | (30.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1365Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.2-0.5 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.6-0.9% I ISO294-4) |
Mechanical Properties
Tensile strength (185.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (12.5KJ/m2 I ISO179 Conditioned | 1.0J |
Flexural Strength (270MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (8364 MPa I ISO178) Conditioned | 2mm/ min |
Thermal Property
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (250*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation!