Polyamide 66, reinforced with 15% of glass fiber and flame resistance halogens, is extruding by twin-screw extruder is PA66 GF15 halogenated FR.
PA66 15% glass fiber and halogens flame retardant modified grades are applied to flame resistance structural parts of the electrical, electronic and power industry, offering low cost, high appearance and easy to shape. It is a good choice of raw material for the power tool lawn mower housing.
Physical Property
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1450Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.4-0.6 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.8-1.2% I ISO294-4) |
Mechanical Properties
Tensile strength (130.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.3% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (6.5KJ/m2 I ISO179) Conditioned | 1.0J |
Flexural Strength (200MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (6500MPa I ISO178) Conditioned | 2mm/min |
Thermal Property
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (240*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | 1.6mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！