PA 6 GF50 is a fiber reinforced plastic made of nylon 6 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added.
PA6 GF50 is used to manufacture high-strength and high wear-resistant structural parts of machinery, vehicles, electronics, sports equipment and other fields. We know that PA6 GF50 composite material takes both strength and toughness into consideration, which is exactly what the suspension control arm needs.
PA6 GF50 (A1011J) is commonly used in the manufacturing of automotive parts, including engine covers, air intake systems, and fuel system components. Its high strength and stiffness make it ideal for applications that require durability and resistance to wear and tear.
Due to its excellent electrical properties and resistance to high temperatures, PA6 GF50 (A1011J) is used in the manufacturing of electrical components such as connectors, switches, and housings.
PA6 GF50 (A1011J) is used in the manufacturing of various industrial machinery components, such as gears, bearings, and conveyor parts. Its high strength and stiffness make it ideal for applications that require durability and resistance to wear and tear.
PA6 GF50 (A1011J) is used in the manufacturing of sports equipment such as tennis rackets, hockey sticks, and ski bindings. Its lightweight and high stiffness make it ideal for applications that require high performance and precision.
Using PA6GF50 material in your products offers numerous benefits, including:
PA6GF50 material is known for its high strength and stiffness, making it an excellent choice for applications where strength is a critical factor.
Due to its resistance to wear and tear, PA6GF50 material is highly durable and can withstand harsh environments and heavy use
PA 6 GF50 material is lightweight compared to many other materials, making it an excellent choice for applications where weight reduction is essential.
By reducing the weight of your products with PA 6 GF50 material, you can increase their energy efficiency, which can result in significant cost savings over time.
PA 6 GF50 material is resistant to many chemicals and can withstand exposure to harsh environments without corroding.
PA 6 GF50 material is highly resistant to dimensional changes caused by temperature fluctuations or humidity, which makes it ideal for applications where precise tolerances are essential.
PA6 GF50 material is a more eco-friendly alternative to many other materials, as it can be recycled and is made from sustainable resources.
Physical Property
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1250Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.5-0.7 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.7-1.1% I ISO294-4) |
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 1.0J |
Notched Impact Strength (125 0MPa I ISO527) Conditioned | 2mm/min |
Flexural Strength (190MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (5700 MPa I ISO178) Conditioned | 5mm/ min |
Thermal Property
Melting Point | (220°C I ISO11357) |
Hot Deformation Temperature | (175*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 240-260°C |
Nozzle Temperature | 240-260*C |
Tooling Temperature | 80*C |
PA6 50 GF (A1011J) can typically withstand temperatures ranging from -40°C to 120°C.
Yes, PA6 50 GF (A1011J) can be colored or dyed using various methods, which can give it an aesthetically pleasing appearance for consumer goods applications.
PA6 GF50 (A1011J) has a relatively low water absorption rate, typically around 1-2%, which contributes to its dimensional stability.
PA6 50 GF (A1011J) is PA6 resin that has been reinforced with glass fiber, which increases its strength and stiffness compared to regular PA6.