Anmei engineers added a certain amount of rubber or elastomer to 30% Glass-Filled nylon66, to double its impact strength. Toughening the elastomer can effectively improve the impact resistance and low temperature performance of nylon.
PA66 GF30 toughening is widely used in gears of industrial products structural parts, and daily necessities structural parts, such as motor gears and electric valves.
Physical Property
Ash | (30.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1300Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.2-0.5 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.6-0.9% I ISO294-4) |
Mechanical Properties
Tensile strength (164.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (3.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (15.8KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (255MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (8169 MPa I ISO178) Conditioned | 2mm/ min |
Thermal Property
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (240*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！