PA66 GF20 heat stabilized is the reinforce polyamide 66 by mixing the glass fiber of 20%, it can be in different colors with excellent higher temperature resistance comprehensive properties.
PA66 20% glass fiber and heat stabilized mixed modified grades are very popular to the mechanical parts, clutch brackets, & electrical devices, offering heat resistance and high mechanical strength.
Physical Property
Ash | (20.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1280Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.5-0.9 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.8-1.1% I ISO294-4) |
Mechanical Properties
Tensile strength (142.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (7.8KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (234MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (6869 MPa I ISO178) Conditioned | 2mm/min |
Thermal Property
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (245*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！