Manufacturers usually add flame retardants to the masterbatch to change the properties of the material. The flame retardant is added to the synthetic polymer by a machine mixing method so that the polymer reaches the characteristics of being difficult to burn. At present, flame retardants in flame retardant PA6 mainly include halogen flame retardants and non-halogen flame retardants, organic flame retardants and inorganic flame retardants.
Our engineers have the expertise to formulate plastics to meet the performance criteria that are necessary for your application.
Flame-retardant modified PA6 (PA6 FR) is mainly suitable for high-temperature environments and is widely used in power tools, household appliances, automobiles and other industries.
Physical Property of Nylon 6 PA6 FR
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1200Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (1.0-1.3 % 1 ISO294-4) |
Shrinkage Vertical Flow | (1.0-1.3% I ISO294-4) |
Mechanical Properties of Nylon 6 PA6 FR
Tensile strength (75.0MPa 1 ISO527) Conditioned | 50mm/min |
Tensile Strain at Break (6.0% I ISO527) Conditioned | 50mm/min |
Notched Impact Strength (4.0KJ/m2 ISO179) Conditioned | 1.0J |
Flexural Strength (108MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (3200 MPa I ISO178) Conditioned | 2mm/min |
Thermal Property of Nylon 6 PA6 FR
Melting Point | (220°C I ISO11357) |
Hot Deformation Temperature | (205*C I ISO75) |
Conditioned | 0.45MPa |
Flammability Class | (HB 1UL94) |
Conditioned | 1.6mm |
Injection Molding Conditions of Nylon 6 PA6 FR
Drying Temperature | 90°C |
Drying Time | 3h |
Cylinder Temperature | 220-240°C |
Nozzle Temperature | 220-240*C |
Tooling Temperature | 80*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！